Vickers and Knoop indentation microhardness study of β-SiAlON ceramic
Acta Physica Polonica A, cilt.120, sa.6, ss.1026-1033, 2011 (SCI-Expanded, Scopus)
- Yayın Türü: Makale / Tam Makale
- Cilt numarası: 120 Sayı: 6
- Basım Tarihi: 2011
- Doi Numarası: 10.12693/aphyspola.120.1026
- Dergi Adı: Acta Physica Polonica A
- Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
- Sayfa Sayıları: ss.1026-1033
- Açık Arşiv Koleksiyonu: AVESİS Açık Erişim Koleksiyonu
- Hatay Mustafa Kemal Üniversitesi Adresli: Evet
Özet
In this paper, analysis and interpretation of mechanical property measurements of β-SiAlON ceramic were reported. Indentation microhardness of β-SiAlON ceramic was measured using the Knoop and Vickers indenters. The analysis of the Vickers indentation microhardness data reveals the reverse indentation size effect that is the apparent microhardness increases with increasing applied indentation test load. However, the Knoop indentation microhardness data exhibit indentation size effect that is the apparent microhardness increases with decreasing applied test load. The experimental Knoop microhardness data was analyzed using Meyer's law, elastic-plastic deformation model, proportional specimen resistance model, and Hays-Kendall's model. As a result, modified proportional specimen resistance model is found to be the most effective one for the load-independent (HLI) microhardness determination of the SiAlON ceramic. It was seen that different models used to analyze the data obtained from the Vickers indentation do not give the same intrinsic hardness value. We also present the calculation of the Young modulus, E, of the β-SiAlON ceramic.