JOURNAL OF CLINICAL PEDIATRIC DENTISTRY, cilt.48, sa.5, ss.131-137, 2024 (SCI-Expanded)
Recently, interest in tooth-colored fluoride-releasing dental materials has increased. Although physical and mechanical properties such as surface hardness, elastic modulus and surface roughness of the restorative materials have been investigated, the effect of different immersion media on these properties is still controversial. The aim of this study was to evaluate the nanohardness, elastic modulus and surface roughness of the fluoride release of tooth-colored restorative materials after immersion in acidic beverages. Prepared samples of three restorative materials (a highly viscous glass ionomer (EQUIA Forte; GC, Tokyo, Japan), a compomer (Dyract XP; Dentsply, Weybridge, UK), and a bioactive restorative material (Activa BioACTIVE; Pulpdent, MA, USA)) were randomly divided and immersed in distilled water, a cola and an orange juice for one week. The HYSITRON T1 950 TriboIndenter device (Hysitron, USA) with the Berkovich diamond indenter tip was used for all measurements. The nanohardness and elastic modulus of the samples were measured by applying a force of 6000 mu N to five different points on the sample surface. Surface roughness measurements were evaluated on random samples by scanning five random 40 x 40 mu m areas. The properties were measured at the initial and one week after immersion. The values of nanohardness, elastic modulus and surface roughness were tested for significant differences using a two-way analysis of variance (ANOVA) with repeated measures (p <0.05). Tukey's honest significant difference (HSD) test was used for multiple comparisons. AB (Activa BioACTIVE) had the highest initial mean values for nanohardness. After postimmersion, the highest mean value for elastic modulus was the initial AB value. The lowest mean value for roughness of 100.36 nm was obtained for the initial DX (Dyract XP) measurement. Acidic beverages had a negative effect on the nanohardness, elastic modulus and surface roughness of the restorative materials.