The formation of passive layers on zinc based platings

Creative Commons License

ÖZYILMAZ A. T., ÖZYILMAZ G., KARAHAN İ. H.

Acta Chimica Slovenica, cilt.63, sa.4, ss.809-821, 2016 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 63 Sayı: 4
  • Basım Tarihi: 2016
  • Doi Numarası: 10.17344/acsi.2016.2690
  • Dergi Adı: Acta Chimica Slovenica
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.809-821
  • Anahtar Kelimeler: Alloy coatings, Corrosion protection, EIS, Electrodeposition, Passivation, Zinc
  • Hatay Mustafa Kemal Üniversitesi Adresli: Evet

Özet

Zinc-iron (ZnFe) and zinc-iron-cobalt (ZnFeCo) platings were achieved on carbon steel applying 3 mA current values. Then, oxalate (OX) and tartrate (Tart) passive layers obtained in sodium oxalate and sodium tartrate medium were formed on carbon steel, ZnFe and ZnFeCo plated carbon steel. SEM images showed that the passive layers on CS, CS/ZnFe and CS/ZnFeCo electrodes exhibited different crystal structures. Corrosion tests revealed that the ZnFeCo particles provided a significant barrier efficiency on CS layer when compared with ZnFe alloy plating. Furthermore, OX layers on ZnFe and ZnFeCo plated carbon steel electrodes exhibited better physical barrier behavior on than those of Tart layers in longer periods.